Polymer Nation F-00 Pigmented 100% Solids Epoxy

Polymer Nation F-00 is most often used as a pigmented broadcast resin and topcoat for resinous concrete flooring projects but it also performs well as a slower curing pigmented primer, and as a slower setting patching material when combined with PN 1324 or PN1329 aggregate.

Color Chart

SKU: N/A Categories: ,

Description

Polymer Nation F-00 consist of a low viscosity, nonylphenol-free, TIO2-filled, epoxy resin (E1W) with our robust modified cycloaliphatic amine reactant (H1). This combination achieves a high-hiding, pigmented epoxy with good flow and leveling, characteristics. The cured material has good broad-range chemical resistance as well as good abrasion and impact resistance.

Description Results Notes
Kit Yield in Gallons 3, 15, 165 Special packaging is available based on size of order and time constraints
Number of Components 2
Mix Ratio Liquids by Volume 2:1 It is always preferred to mix the entire kit, whenever possible, to avoid off-ratio mixtures
Ideal Application Temperatures 60F-90F Verify that substrate temperature is above 5 degrees of dewpoint during application and cure of material to avoid a potential amine blush
Mixed Viscosity in cP@25C/77F 500-600 Warmer temperatures will reduce viscosity and lower temperatures will increase viscosity
Gel Time S/M/F 45/30/15 min. Warmer temperatures will decrease gel time and lower temperatures will increase gel time
Dry to Touch S/M/F 4/3/2 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Through Dry S/M/F 10/7/5 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Dry to Walk S/M/F 12/8/6 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Dry to Lightly Use S/M/F 24/16/12 Hours Warmer temperatures will reduce time and colder temperatures will increase time
Full Cure 7 Days Warmer temperatures will reduce time and colder temperatures will increase time
Shore Hardness at 24 hours D65 Warmer temperatures will increase hardness
Shore Hardness at 7 days D78 Warmer temperatures will shorten time to reach full hardness
Gloss @ 60 Degree Angle 90+ Applying material close to dew point will decrease gloss and may result in an amine blush
VOC’s of Mixed Material <50g/L EPA Method 24
Color Scale per ASTM D1500 .5-1.0 Clear to slightly amber before colorants are introduced
Solids by Volume Mixed 100%
Storage 60F-90F Store material between 60-90 degrees F in a protected dry location.
Odor Subtle Measuring odor offensiveness is difficult so experience with chemicals has been consulted here
Application Thickness in Mils As a primer 8-12. As a body coat 12-20. As a topcoat 10-16
Disposal Dispose of  material, containers, solvents, etc. per Federal, State and local guideline, rules and laws
Available Colors White, Light Gray Medium Gray and Warm Sun
Mixing & Installation Combine all of part A and B into a single container, large enough to accept the entire kit. Mix at 350 RPM for 2-3 minutes using an appropriate mixing blade and making sure not to introduce excessive air into the solution. Pour the entire content from the container onto the floor and follow normal squeegee and back roll techniques. To make an epoxy patching material mix no more material than can be mixed and applied within the stated Gel time and add the selected aggregate until the desired thickness is achieved. Recoat within 24 hours. Clean tools with a solvent similar to Xylene or Acetone.
Polymer Nation believes the information contained herein to be true and accurate. Information contained herein is for evaluation purposes only.

 

Additional information

F-00 Packaging

3 Gallon Kit, 15 Gallon Kit

Color

White C-18, Light Gray C-03, Medium Gray C-02, Warm Sun C-16